A Displacement-energy Model Approach for Evaluating the Interfacial Stress in Multilayer Film Structures Based on the Interactions of Grains at the Interface

Received: 25 September 2021     Accepted: 22 October 2021     Published: 24 November 2021
Views:       Downloads:
Abstract

For multilayer film structures, mechanical failure is usually taken place at the interface. To deeply understand the typical issue, it is first essential to know the stress status at the interlayer surface. For this aim, in this work, the author presented displacement-energy models (DEM) for accurately calculating the interfacial stress in multilayer film structures and the impact of the morphology and size of the interacting grains at the interface. The stress-inducing mechanisms are related to the displacement-energy phenomenon of the interacting grains in the structure caused by the deposition technique. In contrast, the interfacial residual stress-evolution in the deposited films is determined from the change in the lattice constant between interacting grains as a function of temperature and time during the deposition and cool-down process. The interacting grains understudied have different morphology with flat and curved surfaces and sizes. Concerning the yttrium barium copper oxide (YBCO) films deposited on the lanthanum aluminum oxide (LaAlO3) substrate, the computed results showed that the morphology and size of the interacting grains affect the net interfacial residual stresses in the YBCO films significantly. Also, the results of the DEM models agree well with the measured value by the X-ray diffraction method (XRD). Specifically, the computed stress in the YBCO films for the interacting grains with spherical surfaces is 0.18 GPa. Similarly, that measured by the XRD method is 0.178± 0.053 GPa. In the future, the findings of this study could be essential in the defect inspection of several Multilayer Engineering Materials, including composites for various applications, which often consist of grains with different morphology and size.

Published in Colloid and Surface Science (Volume 6, Issue 1)
DOI 10.11648/j.css.20210601.12
Page(s) 8-15
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2021. Published by Science Publishing Group

Keywords

Displacement-energy Model (DEM) Approach, Interfacial Stress, Grains Interactions, Yttrium Barium Copper Oxide (YBCO) Crystal

References
[1] Mbam, S. O., Nwonu, S. E., Orelaja, O. A., Nwigwe, U. S., Gou, X-F. Thin-film coating; historical evolution, conventional deposition technologies, stress-state micro/nano-level measurement/models and prospects projection: a critical review. Materials Research Express, 6 (12) 122001, (2019).
[2] Ogata, M., Miyazaki, Y., Hasegawa, H., Sasakawa, T., Nagashima, K. Basic study of HTS magnet using 2G wires for maglev train. Physica C: Superconductivity and its Applications, 470, 1782-6, (2010).
[3] Bernstein, P., Noudem, J. Superconducting magnetic levitation: principle, materials, physics, and models. Superconductor Science and Technology, 33, 033001, (2020).
[4] Ikeda, R., Ota, S., Aiba, M., Yoda, H., Watanabe, K. Insulation Diagnosis with a Focus on Partial Discharge of the Propulsion Coils of the Superconducting Maglev. Quarterly Report of RTRI, 61, 66-71, (2020).
[5] Dong, F., Huang, Z., Xu, X., Wang, M., Teng, X., Hao, L., et al. Method and Process of Mechanical Evaluation of a 2G HTS Magnet System for Maglev Applications. IEEE Transactions on Applied Superconductivity, 30, 1-5, (2020).
[6] Lee, T. D., Ebong, A. U. A review of thin-film solar cell technologies and challenges. Renewable and Sustainable Energy Reviews, 70, 1286-97, (2017).
[7] Chopra, K, A Technical Review on the Thin-Films Coatings for Enhancing the Efficiency of the Photo-Voltaic Cells for Solar Energy Applications. Invertis Journal of Renewable Energy, 2, 199-207, (2012).
[8] Xue, D-J., Liu, S-C., Dai, C-M., Chen, S., He, C., Zhao, L., et al. GeSe thin-film solar cells fabricated by self-regulated rapid thermal sublimation. Journal of the American Chemical Society, 139, 958-65, (2017).
[9] Jeong, E. G., Lim, M. S., Choi, K. C. P-129: Zero-Stress Thin-film Encapsulation Method for Increasing the Intrinsic Stability of Flexible OLEDs. SID Symposium Digest of Technical Papers, Wiley Online Library, 1746-9, (2017).
[10] Abadias, G., Chason, E., Keckes, J., Sebastiani, M., Thompson, G. B., Barthel, E., et al. Stress in thin films and coatings: Current status, challenges, and prospects. Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films, 36, 020801, (2018).
[11] Korzeniewska, E., Szczęsny, A. Parasitic parameters of thin-film structures created on flexible substrates in PVD process. Microelectronic Engineering, 193, 62-4, (2018).
[12] Xia, W., Song, J., Hsu, D. D., Keten, S. Understanding the interfacial mechanical response of nanoscale polymer thin films via nanoindentation. Macromolecules, 49, 3810-7, (2016).
[13] Li, Z-X., Cao, J-J., Gou, X-F., Wang, T-G., Xue, F. Uncovering a new quasi-2D CuO2 plane between the YBa2Cu3O7 and CeO2 buffer layer of coated conductors. Applied Surface Science, 427, 169-73, (2018).
[14] Mbam, S. O., Gou, X-F. An analytical method for predicting the net (thermal plus intrinsic) residual stresses in multilayered yttrium barium copper oxide coated conductors. Materials Research Express, 6, 096002, (2019).
[15] Sugino, C., Ruzzene, M., Erturk, A. An analytical framework for locally resonant piezoelectric metamaterial plates. International Journal of Solids and Structures, 182, 281-94, (2020).
[16] Cheikh, I. B., Parry, G., Dalmas, D., Estevez, R., Marthelot, J. Analysis of the multi-cracking mechanism of brittle thin films on elastic-plastic substrates. International Journal of Solids and Structures, 180, 176-88, (2019).
[17] Mikula, J., Joshi, S. P., Tay, T-E., Ahluwalia, R., Quek, S. S. A phase-field model of grain boundary migration and grain rotation under elastoplastic anisotropies. International Journal of Solids and Structures, 178, 1-18, (2019).
[18] Mbam, S. O., Jiang, Z-F., Gou, X-F. A displacement-energy model of studying the delaminating behavior of multi-layer REBCO coated conductor tapes. Physica C: Superconductivity and its Applications, 560, 10-8, (2019).
[19] Chason, E., Shin, J., Hearne, S., Freund, L. Kinetic model for dependence of thin-film stress on growth rate, temperature, and microstructure. Journal of Applied Physics, 111, 083520, (2012).
[20] Chason, E., Karlson, M., Colin, J., Magnfält, D., Sarakinos, K., Abadias, G. A kinetic model for stress generation in thin films grown from energetic vapor fluxes. Journal of Applied Physics, 119, 145307, (2016).
[21] Mbam, S. O., Gou, X-F. Inspection of Fabrication Defects in REBCO Coated Conductors from Various Industrial Manufacturers under Similar Fabrication Conditions using the DEM Approach. Physica C: Superconductivity and its Applications, 1353664, (2020).
[22] Mbam, S. O., Gou, X-F. Fabrication stacking faults and its influence on the delamination behavior of SuperPower (SCS4050®) tapes. Engineering Failure Analysis, 104609, (2020).
[23] Mbam, S. O., Gou, X-F. Uncovering and elimination of the natural separation of interacting molecules of standard REBCO crystals, a panacea for improvement of its delamination strength. Engineering Failure Analysis, 107, 104196, (2020).
[24] Hsueh, C., Paranthaman, M. Analytical modeling of residual stresses in multilayered superconductor systems. Journal of Materials Science, 43, 6223-32, (2008).
[25] Cheon, J. H., Shankar, P. S, Singh, J. P. Influence of processing methods on residual stress evolution in coated conductors. Superconductor Science and Technology, 18, 142-6, (2005).
[26] Xiong, J., Qin, W., Cui, X., Tao, B., Tang, J., Li, Y. Effect of processing conditions and methods on residual stress in CeO2 buffer layers and YBCO superconducting films. Physica C: Superconductivity and its Application, 442, 124-8, (2006).
[27] Xu, Y., Shi, D. A review of coated conductor development. Tsinghua science and technology, 8, 342-69, (2003).
[28] Ghidelli, M., Sebastiani, M., Collet, C., Guillemet, R. Determination of the elastic moduli and residual stresses of freestanding Au-TiW bilayer thin films by nanoindentation. Materials & Design, 106, 436-45, (2016).
[29] Korsunsky, A. M., Sebastiani, M., Bemporad, E. Residual stress evaluation at the micrometer scale: Analysis of thin coatings by FIB milling and digital image correlation. Surface and Coatings Technology, 205, 2393-403, (2010).
Cite This Article
  • APA Style

    Stephen Ogbonna Mbam. (2021). A Displacement-energy Model Approach for Evaluating the Interfacial Stress in Multilayer Film Structures Based on the Interactions of Grains at the Interface. Colloid and Surface Science, 6(1), 8-15. https://doi.org/10.11648/j.css.20210601.12

    Copy | Download

    ACS Style

    Stephen Ogbonna Mbam. A Displacement-energy Model Approach for Evaluating the Interfacial Stress in Multilayer Film Structures Based on the Interactions of Grains at the Interface. Colloid Surf. Sci. 2021, 6(1), 8-15. doi: 10.11648/j.css.20210601.12

    Copy | Download

    AMA Style

    Stephen Ogbonna Mbam. A Displacement-energy Model Approach for Evaluating the Interfacial Stress in Multilayer Film Structures Based on the Interactions of Grains at the Interface. Colloid Surf Sci. 2021;6(1):8-15. doi: 10.11648/j.css.20210601.12

    Copy | Download

  • @article{10.11648/j.css.20210601.12,
      author = {Stephen Ogbonna Mbam},
      title = {A Displacement-energy Model Approach for Evaluating the Interfacial Stress in Multilayer Film Structures Based on the Interactions of Grains at the Interface},
      journal = {Colloid and Surface Science},
      volume = {6},
      number = {1},
      pages = {8-15},
      doi = {10.11648/j.css.20210601.12},
      url = {https://doi.org/10.11648/j.css.20210601.12},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.css.20210601.12},
      abstract = {For multilayer film structures, mechanical failure is usually taken place at the interface. To deeply understand the typical issue, it is first essential to know the stress status at the interlayer surface. For this aim, in this work, the author presented displacement-energy models (DEM) for accurately calculating the interfacial stress in multilayer film structures and the impact of the morphology and size of the interacting grains at the interface. The stress-inducing mechanisms are related to the displacement-energy phenomenon of the interacting grains in the structure caused by the deposition technique. In contrast, the interfacial residual stress-evolution in the deposited films is determined from the change in the lattice constant between interacting grains as a function of temperature and time during the deposition and cool-down process. The interacting grains understudied have different morphology with flat and curved surfaces and sizes. Concerning the yttrium barium copper oxide (YBCO) films deposited on the lanthanum aluminum oxide (LaAlO3) substrate, the computed results showed that the morphology and size of the interacting grains affect the net interfacial residual stresses in the YBCO films significantly. Also, the results of the DEM models agree well with the measured value by the X-ray diffraction method (XRD). Specifically, the computed stress in the YBCO films for the interacting grains with spherical surfaces is 0.18 GPa. Similarly, that measured by the XRD method is 0.178± 0.053 GPa. In the future, the findings of this study could be essential in the defect inspection of several Multilayer Engineering Materials, including composites for various applications, which often consist of grains with different morphology and size.},
     year = {2021}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - A Displacement-energy Model Approach for Evaluating the Interfacial Stress in Multilayer Film Structures Based on the Interactions of Grains at the Interface
    AU  - Stephen Ogbonna Mbam
    Y1  - 2021/11/24
    PY  - 2021
    N1  - https://doi.org/10.11648/j.css.20210601.12
    DO  - 10.11648/j.css.20210601.12
    T2  - Colloid and Surface Science
    JF  - Colloid and Surface Science
    JO  - Colloid and Surface Science
    SP  - 8
    EP  - 15
    PB  - Science Publishing Group
    SN  - 2578-9236
    UR  - https://doi.org/10.11648/j.css.20210601.12
    AB  - For multilayer film structures, mechanical failure is usually taken place at the interface. To deeply understand the typical issue, it is first essential to know the stress status at the interlayer surface. For this aim, in this work, the author presented displacement-energy models (DEM) for accurately calculating the interfacial stress in multilayer film structures and the impact of the morphology and size of the interacting grains at the interface. The stress-inducing mechanisms are related to the displacement-energy phenomenon of the interacting grains in the structure caused by the deposition technique. In contrast, the interfacial residual stress-evolution in the deposited films is determined from the change in the lattice constant between interacting grains as a function of temperature and time during the deposition and cool-down process. The interacting grains understudied have different morphology with flat and curved surfaces and sizes. Concerning the yttrium barium copper oxide (YBCO) films deposited on the lanthanum aluminum oxide (LaAlO3) substrate, the computed results showed that the morphology and size of the interacting grains affect the net interfacial residual stresses in the YBCO films significantly. Also, the results of the DEM models agree well with the measured value by the X-ray diffraction method (XRD). Specifically, the computed stress in the YBCO films for the interacting grains with spherical surfaces is 0.18 GPa. Similarly, that measured by the XRD method is 0.178± 0.053 GPa. In the future, the findings of this study could be essential in the defect inspection of several Multilayer Engineering Materials, including composites for various applications, which often consist of grains with different morphology and size.
    VL  - 6
    IS  - 1
    ER  - 

    Copy | Download

Author Information
  • Department of Mechanical/Mechatronic Engineering, Alex Ekwueme Federal University, Ndufu-Alike Ikwo, Abakaliki, Nigeria

  • Sections